RUSTOLEUM COMBICOLOR ORIGINAL SMOOTH ANTI-RUST PRIMER AND TOPCOAT

Anti-rust primer and topcoat in one, based on alkyd resins for direct application onto rust.

Long lifetime
Maximum elasticity
Direct application onto rust
Low odour
Excellent anti-corrosion protection
Excellent one-coat cover Resistant to knocks

Coverage:10.5m²/L
Drying Time:2 hours
Time Between Coats:8-16 hours
Use:INTERIOR & EXTERIOR
Application Method:ROLLER, BRUSH, SPRAY
Thinner:THINNER 7301 (COMBICOLOR)

RUST-OLEUM® CombiColor Metal 7300/7400 coating is primer and topcoat in one, based on
a urethane modified alkyd, providing good drying properties at low temperatures.
The product contains rust-inhibitive pigments and is lead- and chromate free.

RECOMMENDED USES
RUST-OLEUM CombiColor Metal 7300/7400 should be applied on bare, manually derusted or
with CombiPrimer Anti-Corrosion 3369/3380 primed steel. CombiColor Metal is intended for
brush and roller application and can also be applied by air spray.
RUST-OLEUM CombiColor Metal 7300/7400 offers corrosion protection in a light industrial
environment.
For metal structures in a more aggressive industrial environment, prior application of a RUSTOLEUM CombiPrimer Anti-Corrosion 3369/3380 is recommended.

TECHNICAL DATA
Appearance: High gloss, Satin (black and white), Flat (black and white).
Colour: See colour card.
Satin and High gloss are also available as tint base.
Density: High gloss/flat: 1.07 kg/l. ± 0.09 depending on colour
Satin: 1,22 kg/l. ± 0,10 depending on colour
Solids Content: High gloss/flat: 54.6% by volume ± 2.0 depending on colour
Satin: 50,6 volume % ± 2,0 depending on colour
Viscosity: High gloss/flat: 100 - 104 KU / Krebs Stormer Units at 20°C
Satin: 86 - 91 KU /Krebs Stormer Units bij 20°C
Recommended film thickness: 55 µm dry, equals 100 µm wet
VOC-content: 439 g/l max.
Ready-to-use mixture: 495 g/l max.
Category: A/i
EU Limit values: 600g/l (2007) / 500g/l (2010)

Coverage
Theoretical: 10.3m²/l at 55µm dry, depending on colour.
Practical: Practical coverage depends on many factors such as porosity and
roughness of the substrate and material losses during application.

SURFACE PREPARATION
Remove oil, grease and all other surface contaminations by alkaline or high pressure (steam)
cleaning in combination with appropriate detergents. Remove rust scale, loose mill scale,
loose rust and loose coatings by scraping and wire brushing to St 3 (ISO 8501-1 : 1988), light
blast cleaning or sanding. Sand intact coatings to roughen the surface slightly.
The surface must be clean and dry during application. Galvanised, Zinc and Alu